Hayacoat UV(Clear/1kg) (AU-L1000OB)
Solvent-free HAYAKOAT UV for VOC control
- Aerosol and Chemical Products
- Conformal Coating for Moisture-resistant and Anti-corrosive
- RoHS compliant
Prices have been revised effective July 1, 2023.
This is a UV-curable insulating coating agent with excellent resistance to moisture and corrosive gases. It contains a fluorescent agent that reacts to black light, making it easy to visually check the coated area. Since it is a UV curable type, it cures in a few seconds to a few dozen seconds, enabling a significant reduction in working time. The formed coating film has excellent insulation properties and improves the insulation reliability of narrow patterns on printed circuit boards. Protects PCBs from salt damage in corrosive gas atmospheres such as hot spring areas and coastal areas. Four variations are available in different content volumes and colors.Hayacoat UVSee the variation of
Main specifications
- Model No.
- AU-L1000OB
- RoHS directive (10 substances)
- Compliant
- Quantity
- 1 piece
- NET
- 1kg (850ml)
- Product size (including packaging, approx.)
- Φ100×190mm
- Weight (including packaging, approx.)
- 1.1kg
- JAN code
- 4931442415045
- Country of origin
- Japan
- Main ingredients
- Acrylate resin
- Appearance
- Clear colorless viscous liquid
- Volume resistivity
- 1.8×1014ohm-cm
- Dielectric Constant
- 4.1 (1MHz)
- Dissipation Factor
- 4.5×10-2(1MHz)
- Dielectric breakdown strength
- 8.8kV/0.1mm
- Copper plate corrosion test
- No discoloration (room temperature, 24h)
- Adhesion
- 100/100 (Cross-cut method on copper foil plate)
- Transmission humidity
- 40.9 (g/m)2D, 100 μm)
- Sulfurous acid gas resistance test
- No corrosion on copper plate surface (30±2ppm, 48h)
- Hydrogen sulfide gas resistance test
- No corrosion on copper plate surface (30±6ppm, 48h)
- Heat and humidity resistance test
- No corrosion on copper foil surface (80°C, 90%, 168h)
- Thermal shock test
- No peeling or cracking (-40°C to 125°C, 100 cycles)
- High temperature test
- No effect on insulation resistance and permeation humidity (150°C, 240h)
- viscosity
- 2100 mPa-s (20°C)
- Specific gravity
- 1.17（20℃）
- Continuous operating temperature range
- -40～125℃
- Hazardous Materials and Content under Fire Service Law
- Class 4 Petroleums No. 3 (non-water soluble) 850ml
- Odor
- Acrylic odor
- Curing Time
- Reference condition] High-pressure mercury lamp: 5mW/cm2 20 seconds, LED UV365nm: 2600mW/cm2 5 sec.
- Approximate area that can be applied
- If the film thickness is 40 µm, the estimated coating area is approximately 20 m.2
aul1000ob